Durus White (PP Like)

Durus White PP Like

DurusWhite ist ein dem Polypropylen ähnliches Photopolymer. DurusWhite ist ideal für vielfältige Anwendungen, bei denen das Aussehen, die Dehnbarkeit und die typische Härte von Polypropylen gefordert sind. Besondere Eigenschaften sind: Izod-Kerbschlagzähigkeit von 44 J/m, Bruchdehnung 44%, Biegemodul 1026 MPa.

Mechanical Properties Test Method English Metric
Tensile Strength ASTM D638-03 2,900-4,350 psi 20-30 MPa
Tensile Modulus ASTM D638-04 145,000-175,000 psi 1,000-1,200 MPa
Tensile Elongation ASTM D638-05 40-50% 40-50%
Flexural Strength ASTM D790-03 4,350-5,800 psi 30-40 MPa
Flexural Modulus ASTM D790-04 175,000-230,000 psi 1,200-1,600 MPa
IZOD Impact, notched ASTM D256-06 0.749-0.937 ft-lb/in 40-50 J/m
Thermal Properties Test Method English Metric
HDT @ 0.45 MPa ASTM D648-06 99-108°F 37-42°C
HDT @ 1.82 MPa ASTM D648-07 90-93°F 32-34°C
Glass Transition Temp. (Tg) DMA E» 95-99°F 35-37°C
Other Test Method Value Available Colors
Shore Hardness (D) Scale D 74-78
Opal White
Rockwell Hardness Scale M No Data
Polymerized density ATSM D792 1.15-1.17 g/cm3
Ash content USP281 0.10-0.12 %
Water absorption, % D570-98 24hr 1.5-1.9 %

The information presented are typical values intended for reference and comparison purposes only. They should not be used for design specifications or quality control purposes.
End-use material performance can be impacted (+/-) by, but not limited to, part design, end-use conditions, etc. Actual values will vary with build conditions.
Product specifications are subject to change without notice.
The performance characteristics of these materials may vary according to application, operating conditions, or end use. Each user is responsible for determining that the material is safe, lawful and technical suitable for the intended laws and regulations. Zare makes no warranties of any kind, express or implied, including, but not limited to, the warranties of merchantability, fitness for a particular use, or warranty against patent infringement.
All information contained in this document were supplied by Stratasys Inc. Copyright© 2013
All Trademarks included in this document are property of the respective owner